Product Details:
|
| Type: | Circular SAW BLADE | Finishing: | Painted |
|---|---|---|---|
| Blade Material: | ALLOY STEEL | Material: | High Speed Steel |
| Product Name: | HSS Circular Saw Blade For Cutting | Usage: | Metal Cutting |
| Advantage: | Long Life | Package: | Carton Box |
| Color: | Customised | Name: | HSS Circular Saw Blade |
| Thickness: | 1.8-3.0mm | Performance: | Fast Sharp Cutting Wood And Laminated Mdf Board |
| Feature: | High Speed.Straight Smooth Edge | Shape: | Segmented |
| Segment Height: | 9/10mm | ||
| High Light: | High Speed HSS Circular Saw Blade,HSS metal cutting circular saw blade,Segmented HSS Circular Saw Blade |
||
HSS circular saw blade with very good durability and high speed
PRODUCTS DESCRIPTION
1. Multi saw blade
2. High finish cutting surface, suitable for ripping all kinds nature wood ,soft /hard wood, dry and wet wood
3. Anti-kickback fingers maintain safety while limiting chip thickness, allowing for a faster, quieter cut
4. Saw body: 75Cr1/ 65Mn
5. Teeth: K05, K10, K20 etc
6. Alternate top bevel tooth
7. Used on multi ripping saw, single or double sizing machine, profiling machine
8. Nickel Finishing cutting without chip
| M2 M35 M42 Cobalt hss circular saw blade | |
| Type | Metal slitting saw blade |
| Diameter | 80-600mm |
| Bore | 5-40mm |
| Thickness | 0.2-8.0mm |
| Number of Teeth | Coarse pitch,Medium pitch,Fine pitch |
| Type of Making Teeth | Milling,Grinding |
| Coating | Original colour, Nitrogenized,TiN coated,black,etc |
| Material | HSS,M2(HSS-Dmo5)(6542),W18,W9,M42,M35(HSS-Co5%),Tungsten Carbide steel |
| Technoledge | heat treatment |
| Surface Treatment | VAPO,TIN,TICN,TIALN. |
| Tooth form | A/AW/B/BW |
| Application | For cutting various steel material and form such as solid bar, pipe, rail etc. - For cutting various non-ferrous material as like aluminum, copper, bronze, brass of pipe, bar, sash and plate etc. |
Available Sizes:(customized service is available)
| Diameter | Thickness | Diameter | Thickness | Diameter | Thickness | Diameter | Thickness | |||
| 40 | 0.2 | 75 | 0.5 | 90 | 0.8 | 125 | 5.0 | |||
| 1.0 | 0.6-0.8 | 1.5 | 130 | 0.8 | ||||||
| 1.2 | 1.0 | 2.0 | 1.2 | |||||||
| 1.5 | 1.2 | 100 | 0.6 | 2.0 | ||||||
| 2.0 | 1.5 | 1.0 | 150 | 0.8 | ||||||
| 2.5 | 2.0 | 1.2 | 1.0 | |||||||
| 3.0 | 2.5 | 1.5 | 1.2 | |||||||
| 4.0 | 3.0 | 2.0 | 1.5 | |||||||
| 5.0 | 3.5 | 2.5 | 2.0 | |||||||
| 60 | 0.2 | 4.0 | 3.0 | 2.5 | ||||||
| 0.8 | 4.5 | 3.5 | 3.0 | |||||||
| 1.0 | 5.5 | 4.0 | 3.5 | |||||||
| 1.2 | 6.0 | 4.5 | 4.0 | |||||||
| 1.5 | 7.0 | 5.0 | 5.0 | |||||||
| 2.0 | 8.0 | 110 | 0.8 | 6.0 | ||||||
| 2.5 | 9.0 | 1.0 | 160 | 1.0 | ||||||
| 3.0 | 80 | 0.5 | 1.2 | 1.2 | ||||||
| 3.5 | 0.7 | 1.5 | 1.5 | |||||||
| 4.0 | 0.8 | 2.0 | 2.0 | |||||||
| 5.0 | 1.0 | 2.5 | 2.5 | |||||||
| 6.0 | 1.2 | 3.0 | 3.0 | |||||||
| 63 | 0.2 | 1.5 | 3.5 | 3.5 | ||||||
| 0.4 | 2.0 | 4.0 | 4.0 | |||||||
| 0.5 | 2.5 | 4.5 | 4.5 | |||||||
| 1.0 | 3.0 | 5.0 | 5.0 | |||||||
| 1.2 | 3.5 | 125 | 0.8 | 180 | 1.2 | |||||
| 1.5 | 4.0 | 1.2 | 1.5 | |||||||
| 2.0 | 4.5 | 1.5 | 200 | 1.2 | ||||||
| 2.5 | 5.0 | 2.0 | 1.5 | |||||||
| 3.0 | 6.0 | 2.5 | 2.5 | |||||||
| 3.5 | 7.0 | 3.0 | 3.0 | |||||||
| 4.0 | 8.0 | 3.5 | 3.5 | |||||||
| 70 | 0.4 | 9.0 | 4.0 | 4.0 | ||||||
| 0.5 | 90 | 0.6 | 4.5 | 5.0 |
HSS-Dmo5 - DIN: 1.3343 - AISI: M2 - JIS: SKH 51
| Typical chemical composition in % | ||||||
| C | Si | Mn | Cr | Mo | V | W |
| 0.9 | 0.25 | 0.3 | 4.1 | 5 | 1.8 | 5.4 |
| Typical chemical composition in % | |||||||
| C | Si | Mn | Cr | Mo | V | W | Co |
| 0.9 | 0.4 | 0.3 | 4.1 | 5 | 1.9 | 6.4 | 4.8 |